Mechanical properties of modified concrete with recycled marin plastic in replacement of fine agregates

Simple item page
dc.creatorArbelaez-Perez, Oscar Felipe
dc.creatorVenites-Mosquera, Jhon Fismhan
dc.creatorCórdoba-Palacios, Yuliana Marcela
dc.creatorMena-Ramírez, Karol Patricia
dc.date2020-05-30
dc.date.accessioned2023-06-29T13:34:00Z
dc.date.available2023-06-29T13:34:00Z
dc.descriptionPlastic waste and its low recycling rate contribute to environmental pollution, requiring valorization strategies This work presents the design and preparation of traditional and mix concrete with replacement of  2.5%, 5.0%, 7.5% and 10% of fine aggregates by recycled plastic of the ocean. With the prepared concrete mixes, cylindrical specimens of 15cmx30mm in diameterxheight, respectively, were made. Slump, density, compressive strength, and elasticity modulus were evaluated. The results exhibited that an increase in the content of recycled plastic generates a decrease in slump and density, as well as an increase in strength and elastic modulus. Specimens with 7.5% exhibited the highest strength (18.9 MPa) equivalent to 91% of the traditional one (20 MPa). The results gathered would form a part of useful information for recycling plastic waste in the preparation of concrete that requiring moderate strength.Los desechos plásticos marinos y su baja tasa de reutilización contribuyen a la contaminación ambiental, requiriéndose estrategias de valorización. Este trabajo presenta el diseño y la preparación de mezclas de concreto tradicional y con reemplazos del 2.5%, 5%, 7.5% y 10% de los agregados finos por plásticos reciclados del mar. A partir de las mezclas preparadas se elaboraron especímenes cilíndricos de 15cmx30cm de diámetroxaltura, respectivamente. Se evaluó el asentamiento, la densidad, la resistencia y el modulo elástico. Los resultados mostraron que un aumento del contenido de plástico reciclado genera una disminución del asentamiento y la densidad, así como un aumento de la resistencia y del módulo elástico. Los especímenes con sustituciones del 7.5% presentaron la mejor resistencia a compresión (18.19 MPa) equivalente al 90.5% del tradicional (20 MPa). Los resultados encontrados muestran información valiosa para la valorización de desechos plásticos marinos en la elaboración de concretos con resistencias moderadas.en-US
dc.descriptionLos desechos plásticos marinos y su baja tasa de reutilización contribuyen a la contaminación ambiental, requiriéndose estrategias de valorización. Este trabajo presenta el diseño y la preparación de mezclas de concreto tradicional y con reemplazos del 2.5%, 5%, 7.5% y 10% de los agregados finos por plásticos reciclados del mar. A partir de las mezclas preparadas se elaboraron especímenes cilíndricos de 15cmx30cm de diámetroxaltura, respectivamente. Se evaluó el asentamiento, la densidad, la resistencia y el modulo elástico. Los resultados mostraron que un aumento del contenido de plástico reciclado genera una disminución del asentamiento y la densidad, así como un aumento de la resistencia y del módulo elástico. Los especímenes con sustituciones del 7.5% presentaron la mejor resistencia a compresión (18.19 MPa) equivalente al 90.5% del tradicional (20 MPa). Los resultados encontrados muestran información valiosa para la valorización de desechos plásticos marinos en la elaboración de concretos con resistencias moderadas.Plastic waste and its low recycling rate contribute to environmental pollution, requiring valorization strategies This work presents the design and preparation of traditional and mix concrete with replacement of  2.5%, 5.0%, 7.5% and 10% of fine aggregates by recycled plastic of the ocean. With the prepared concrete mixes, cylindrical specimens of 15cmx30mm in diameterxheight, respectively, were made. Slump, density, compressive strength, and elasticity modulus were evaluated. The results exhibited that an increase in the content of recycled plastic generates a decrease in slump and density, as well as an increase in strength and elastic modulus. Specimens with 7.5% exhibited the highest strength (18.9 MPa) equivalent to 91% of the traditional one (20 MPa). The results gathered would form a part of useful information for recycling plastic waste in the preparation of concrete that requiring moderate strength. es-ES
dc.formattext/html
dc.formatapplication/pdf
dc.formatapplication/xml
dc.identifierhttps://revistas.elpoli.edu.co/index.php/pol/article/view/1679
dc.identifier10.33571/rpolitec.v16n31a6
dc.identifier.urihttps://repositorio.elpoli.edu.co/handle/123456789/1057
dc.languagespa
dc.publisherPolitécnico Colombiano Jaime Isaza Cadavides-ES
dc.relationhttps://revistas.elpoli.edu.co/index.php/pol/article/view/1679/1413
dc.relationhttps://revistas.elpoli.edu.co/index.php/pol/article/view/1679/1427
dc.relationhttps://revistas.elpoli.edu.co/index.php/pol/article/view/1679/1527
dc.sourceRevista Politécnica; Vol. 16 No. 31: Enero-Junio, 2020; 77-84en-US
dc.sourceRevista Politécnica; Vol. 16 Núm. 31: Enero-Junio, 2020; 77-84es-ES
dc.sourceRevista Politécnica; v. 16 n. 31: Enero-Junio, 2020; 77-84pt-BR
dc.source2256-5353
dc.source1900-2351
dc.subjectPlastic wasteen-US
dc.subjectmodified concreteen-US
dc.subjectmechanical propertiesen-US
dc.subjectResiduos plásticoses-ES
dc.subjectConcretos modificadoses-ES
dc.subjectPropiedades mecánicases-ES
dc.titleMechanical properties of modified concrete with recycled marin plastic in replacement of fine agregatesen-US
dc.titlePropiedades mecánicas de concretos modificados con plástico marino reciclado en reemplazo de los agregados finoses-ES